725 Каталог KYOCERA 2017 Инструмент сборный и монолитный для станков Стр.L82

Каталог KYOCERA 2017 Инструмент режущий Стр. L82 0725 Lab2u

Recommended Cutting Conditions Рекомендованные режимы резания на станках 3RDSL, 4RDSL, 5RDSL (Shouldering) Applications Workpiece Material Обрабатываемый материал Depth of Cut (apxae) (mm) Outside Dia. Dc (mm) 6 8 10 12 16 20 25 Steel < 22HRC 2.5Dcx0.5Dc Spindle Revolution (min-1) 7,800 5,900 4,700 3,900 2,900 2,300 1,900 Feed Rate (mm/min) 700 700 770 780 840 840 940 22 32HRC 2.5Dcx0.4Dc Spindle Revolution (min-1) 6,700 5,000 4,000 3,400 2,500 2,000 1,600 Feed Rate (mm/min) 500 500 600 600 600 640 720 y 32 40HRC Spindle Revolution (min-1) 4,500 3,400 2,700 2,200 1,700 1,300 1,100 Feed Rate (mm/min) 220 220 290 290 280 280 280 CC 40 45HRC Spindle Revolution (min-1) 3,400 2,500 2,000 1,700 1,300 1,000 800 Feed Rate (mm/min) 150 150 180 180 180 180 180 r ae 45 50HRC 2.5Dcx0.3Dc Spindle Revolution (min-1) 2,900 2,200 1,800 1,500 1,100 900 700 Shouldering Feed Rate (mm/min) 110 110 130 130 120 120 120 Stainless Steel 1.5Dcx0.1Dc Spindle Revolution (min-1) 3,700 2,800 2,200 1,900 1,400 1,100 900 Feed Rate (mm/min) 120 150 200 200 220 200 230 Cast Iron 2.5Dcx0.5Dc Spindle Revolution (min-1) 6,700 5,000 4,000 3,400 2,500 2,000 1,600 Feed Rate (mm/min) 600 600 720 720 720 770 970 Machining with water soluble coolant is recommended for stainless steel. Slotting is not recommended. 4RFSM, 6RFSM End mill Routers Applications Workpiece Material Обрабатываемый материал Application Depth of Cut (apxae) (mm) Outside Dia. Dc(mm) 6 8 10 12 16 4 flutes 6 flutes 20 4 flutes 6 flutes 25 Shouldering Slotting Steel Shouldering 1.5Dcx0.4Dc Spindle Revolution (min-1) 8,000 6,000 4,800 4,000 3,000 3,000 2,400 2,400 35 45HRC Feed Rate (mm/min) Slotting 0.5Dc Spindle Revolution (min-1) 6,400 4,800 3,800 3,200 2,400 2,400 1,900 1,900 Feed Rate (mm/min) 480 480 490 500 500 720 500 750 Shouldering 1.5Dcx0.33Dc Spindle Revolution (min-1) 45 55HRC Feed Rate (mm/min) Slotting 0.5Dc Spindle Revolution (min-1) 4,700 3,500 2,800 2,300 1,800 1,800 1,400 1,400 Feed Rate (mm/min) Shouldering 1.5Dcx0.25Dc Spindle Revolution (min-1) 55 60HRC Feed Rate (mm/min) 190 220 230 240 220 320 230 340 Slotting 0.3Dc Spindle Revolution (min-1) Feed Rate (mm/min) Shouldering 1.5Dcx0.4Dc Spindle Revolution (min-1) 3,700 2,800 2,200 1,900 1,400 1,400 1,100 1,100 Stainless Steel Feed Rate (mm/min) 300 280 260 300 280 420 290 430 Slotting 0.5Dc Spindle Revolution (min-1) Feed Rate (mm/min) 200 190 180 200 190 290 210 310 Shouldering 2Dcx0.4Dc Spindle Revolution (min-1) 3,700 2,800 2,200 1,900 1,400 1,400 1,100 1,100 < 40HRC Feed Rate (mm/min) Slotting 0.5Dc Spindle Revolution (min-1) 3,000 2,200 1,800 1,500 1,100 1,100 900 900 Feed Rate (mm/min) 310 310 310 310 310 470 310 430 Shouldering 1.5Dcx0.25Dc Spindle Revolution (min-1) > 40HRC Feed Rate (mm/min) 300 300 300 300 300 430 300 430 Slotting 0.3Dc Spindle Revolution (min-1) 2,500 1,900 1,500 1,300 1,000 1,000 800 800 Feed Rate (mm/min) Heat'resistant Alloys (Ni'base heat' resistant alloys) Shouldering 1Dcx0.2Dc Spindle Revolution (min-1) Feed Rate (mm/min) 100 100 100 100 100 140 100 140 Slotting 0.25Dc Spindle Revolution (min-1) Feed Rate (mm/min) 1,900 1,500 640 1,100 310 900 380 270 900 700 360 370 600 130 630 630 630 640 640 900 640 930 800 350 350 350 350 350 530 350 530 460 280 280 280 280 280 420 280 420 370 900 260 280 250 800 390 390 390 390 390 590 390 540 450 800 230 230 230 230 230 340 230 340 290 800 600 600 500 500 400 800 600 500 500 400 400 300 80 80 80 80 80 80 Machining with water soluble coolant is recommended for stainless steel, titanium alloys and heat'resistant alloys. L82