679 Каталог KYOCERA 2016 Инструмент режущий станочный Пластины Резцы Фрезы Сверла Стр.L65

Каталог KYOCERA 2016 Режущий инструмент для станков Стр. L65 0679 Lab2u

3RFRS, 4RFRS Applications Workpiece Material Application Depth of Cut (apxae) (mm) Outside Dia. Dc (mm) 65 610 612 Shouldering Slotting Steel <30HRC Shouldering 0.8Dcx0.5Dc Spindle Revolution (min-1) 14,300 11,500 9,600 7,200 Feed Rate (mm/min) 860 860 1,150 1,150 Slotting 0.8Dc Spindle Revolution (min-1) Feed Rate (mm/min) 690 690 920 920 Shouldering 0.8Dcx0.4Dc Spindle Revolution (min-1) 9,600 7,600 6,400 4,800 30 40HRC Feed Rate (mm/min) Slotting 0.8Dc Spindle Revolution (min-1) 7,600 6,100 5,100 3,800 Feed Rate (mm/min) 340 370 490 490 Shouldering 0.8Dcx0.4Dc Spindle Revolution (min-1) 40 50HRC Feed Rate (mm/min) 190 230 320 320 Slotting 0.5Dc Spindle Revolution (min-1) 5,100 4,100 3,400 2,500 Feed Rate (mm/min) Shouldering 0.8Dcx0.25Dc Spindle Revolution (min-1) 50 60HRC Feed Rate (mm/min) 100 100 130 140 Slotting 0.3Dc Spindle Revolution (min-1) Feed Rate (mm/min) Shouldering 0.8Dcx0.2Dc Spindle Revolution (min-1) 3,200 2,500 2,100 1,600 60 70HRC Feed Rate (mm/min) Slotting 0.25Dc Spindle Revolution (min-1) Feed Rate (mm/min) 50 50 60 60 Shouldering 0.8Dcx0.4Dc Spindle Revolution (min-1) 6,400 5,100 4,200 3,200 Titanium Alloys Feed Rate (mm/min) Slotting 0.5Dc Spindle Revolution (min-1) 4,000 3,200 2,700 2,000 Feed Rate (mm/min) 80 100 150 140 5,700 1,150 920 3,800 3,100 490 320 2,000 150 1,300 60 2,500 1,600 160 4,800 1,150 920 3,200 2,500 460 340 1,700 160 1,100 70 2,100 1,300 170 Machining with water soluble coolant is recommended for titanium alloys. 6PFK, 8PFK (Medium) 430 460 640 570 260 260 260 270 80 80 60 60 70 70 80 90 800 230 340 320 350 380 Applications Workpiece Material Application Depth of Cut (apxae) (mm) Outside Dia. Dc (mm) 66 68 610 612 616 620 625 Carbon Steel, Cast Iron Shouldering Dc<620 1.5Dcx0.2Dc Dc>620 1.5Dcx0.1Dc Spindle Revolution (min-1) 7,400 5,600 4,500 3,700 2,800 2,200 1,800 Feed Rate (mm/min) 2,650 2,640 2,410 2,250 2,010 1,700 1,500 Alloy Steel Shouldering Dc<620 1.5Dcx0.2Dc Dc>620 1.5Dcx0.1Dc Spindle Revolution (min-1) 6,400 4,800 3,800 3,200 2,400 1,900 1,500 CC 1 Feed Rate (mm/min) 2,250 2,090 1,950 1,910 1,720 1,450 1,220 Pre-hardened steel (30 38HRC) Shouldering 1.5Dcx0.1Dc Spindle Revolution (min-1) 5,600 4,200 3,300 2,800 2,100 1,700 1,300 Feed Rate (mm/min) 1,780 1,710 1,520 1,400 1,220 1,120 980 Stainless Steel Titanium Alloys Shouldering 1.5Dcx0.05Dc Spindle Revolution (min-1) 5,000 3,800 3,000 2,500 1,900 1,500 1,200 Shouldering Feed Rate (mm/min) 1,350 1,320 1,200 1,130 970 850 720 Machining with water soluble coolant is recommended for stainless steel and titanium alloys. Slotting is not recommended. 6PFK, 8PFK (Long) Applications Workpiece Material Application Depth of Cut (apxae) (mm) Outside Dia. Dc (mm) 66 68 610 612 616 620 625 Caibon Steel, Cast Iron Shouldering 3.0Dcx0.01Dc Spindle Revolution (min-1) 4,600 3,500 2,800 2,300 1,700 1,400 1,100 Feed Rate (mm/min) 1,830 1,730 1,530 1,380 1,120 880 660 Alloy Steel Shouldering 3.0Dcx0.01Dc Spindle Revolution (min-1) 3,700 2,800 2,200 1,800 1,400 1,100 900 CC 1 Feed Rate (mm/min) 1,490 1,340 1,220 1,120 940 720 540 Pre-hardened steel (30 38HRC) Shouldering 3.0Dcx0.01Dc Spindle Revolution (min-1) 2,800 2,100 1,700 1,400 1,100 850 650 £ Feed Rate (mm/min) 920 680 750 670 550 480 390 Stainless Steel Titanium Alloys Shouldering 3.0Dcx0.01Dc Spindle Revolution (min-1) 2,500 1,900 1,500 1,300 950 750 600 Shouldering Feed Rate (mm/min) 700 670 590 540 440 370 290 Machining with water soluble coolant is recommended for stainless steel and titanium alloys. Slotting is not recommended. L65 Solid End Mill