526 Каталог KYOCERA 2016 Инструмент режущий станочный Пластины Резцы Фрезы Сверла Стр.J32

Каталог KYOCERA 2016 Режущий инструмент для станков Стр. J32 0526 Lab2u

Threading Recommended Cutting Conditions KTN / KTNS Workpiece Material Recommended Insert Grades (Cutting Speed Vc: m/min) Cermet PVD Coated Carbide Carbide TC60M PR1115 GW15 Carbon Steel 100 150 100 150 - First ap (Radial) 0.3mm and under 0.3mm and under Alloy Steel 100 150 100 150 - First ap (Radial) 0.3mm and under 0.3mm and under Stainless Steel 60 80 60 80 - First ap (Radial) 0.25mm and under 0.25mm and under Cast Iron 100 First ap (Radial) 0.3mm and under Aluminum 150 400 First ap (Radial) 0.3mm and under Brass 150 300 First ap (Radial) 0.3mm and under KTT Workpiece Material Recommended Insert Grades (Cutting Speed Vc: m/min) Cermet PVD Coated Carbide Carbide TC60M PR930 PR1115 KW10 100 150 100 150 100 150 First ap (Radial) 0.3mm and under 0.3mm and under 0.3mm and under Alloy Steel 100 150 100 150 100 150 - First ap (Radial) 0.3mm and under 0.3mm and under 0.3mm and under Stainless Steel 60 80 60 80 60 80 - First ap (Radial) 0.25mm and under 0.25mm and under 0.25mm and under Cast Iron - 100 First ap (Radial) 0.3mm and under Aluminum - 150 400 First ap (Radial) 0.3mm and under Brass - 150 300 First ap (Radial) 0.3mm and under KTTX / S-KTTX Workpiece Material Recommended Insert Grades (Cutting Speed Vc: m/min) Cermet PVD Coated Carbide Carbide TC60M PR930 PR1115 KW10 100 150 100 150 100 150 First ap (Radial) 0.3mm and under 0.3mm and under 0.3mm and under Alloy Steel 100 150 100 150 100 150 - First ap (Radial) 0.3mm and under 0.3mm and under 0.3mm and under Stainless Steel 60 80 60 80 60 80 - First ap (Radial) 0.25mm and under 0.25mm and under 0.25mm and under Cast Iron - 100 First ap (Radial) 0.3mm and under Aluminum - 150 400 First ap (Radial) 0.3mm and under Brass - 150 300 First ap (Radial) 0.3mm and under SIN / CIN Workpiece Material Recommended Insert Grades (Cutting Speed Vc: m/min) Cermet PVD Coated Carbide Carbide TC60M PR1115 GW15 Carbon Steel 100 150 100 150 - First ap (Radial) 0.3mm and under 0.3mm and under Alloy Steel 100 150 100 150 - First ap (Radial) 0.3mm and under 0.3mm and under Stainless Steel 60 80 60 80 - First ap (Radial) 0.25mm and under 0.25mm and under Cast Iron 100 First ap (Radial) 0.3mm and under Aluminum 150 400 First ap (Radial) 0.3mm and under Brass 150 300 First ap (Radial) 0.3mm and under For 06IR / 08IR, please lower it to a figure under 40% of above condition list S STWP (-E) Workpiece Material Recommended Insert Grades (Cutting Speed Vc: m/min) Cermet PVD Coated Cermet Carbide TN6020 TN60 PV7020 KW10 Carbon Steel 100 150 100 150 100 150 - First ap (Radial) 0.25mm and under 0.25mm and under 0.25mm and under Alloy Steel 100 150 100 150 100 150 - First ap (Radial) 0.25mm and under 0.25mm and under 0.25mm and under Stainless Steel First ap (Radial) Cast Iron - 100 First ap (Radial) 0.25mm and under Aluminum - 150 400 First ap (Radial) 0.25mm and under Brass - 150 300 First ap (Radial) 0.25mm and under KITG Workpiece Material Recommended Insert Grades (Cutting Speed Vc: m/min) Cermet PVD Coated Carbide Carbide TC60M PR930 PR1115 KW10 100 150 100 150 100 150 First ap (Radial) 0.3mm and under 0.3mm and under 0.3mm and under Alloy Steel 100 150 100 150 100 150 - First ap (Radial) 0.3mm and under 0.3mm and under 0.3mm and under Stainless Steel 60 80 60 80 60 80 - First ap (Radial) 0.25mm and under 0.25mm and under 0.25mm and under Cast Iron - 100 First ap (Radial) 0.3mm and under Aluminum - 150 400 First ap (Radial) 0.3mm and under Brass - 150 300 First ap (Radial) 0.3mm and under :1st Recommendation :2nd Recommendation Coolant is recommended. In case of using cermet insert, honing the edge with hand lapper enables higher stability. In case of threading stainless steel, please set two to three passes more than previous description of . J32