99 Каталог TAEGUTEC 2015 Новый металлорежущий инструмент и оснастка Стр.D40

Каталог TAEGUTEC 2015 Новый инструмент и оснастка Стр. D40 0099 Lab2u

Recommended Cutting Conditions Machining data for SPADERUSH ISO Material Condition Tensile strength (N mm2) Hardness HB Material No. Cutting speed Vc(m min) 0.25%C Annealed 420 125 1 80-140 Non-alloy steel 0.25%C Annealed 650 190 2 80-130 cast steel free 0.55%C Quenched and tempered 850 250 3 80-120 cutting steel 0.55%C Annealed 750 220 4 70-110 Quenched and tempered 1000 300 5 50-90 P Low alloy steel and cast steel Annealed 600 200 6 80-120 930 275 7 70-110 (Less than 5% of Quenched and tempered 1000 300 8 50-90 alloying elements) 1200 350 9 40-70 High alloy steel cast steel Annealed 680 200 10 50-90 and tool steel Quenched and tempered 1100 325 11 40-80 Stainless steel and cast steel Ferritic martensitic 680 200 12 40-70 M Martensitic 820 240 13 40-70 Austenitic 600 180 14 30-70 Gray cast iron Ferritic 160 15 90-180 (GG) Pearlitic 250 16 80-140 K Cast iron nodular Ferritic 180 17 90-165 (GGG) Pearlitic 260 18 80-140 Malleable cast iron Ferritic 130 19 90-160 Pearlitic 230 20 80-140 Aluminum - Wrought alloy Not cureable 60 21 90-220 Cured 100 22 90-220 12% Si Not cureable 75 23 90-220 T - um- in II Cured 90 24 90-220 N 12% Si High temp. 130 25 80-160 1% Pb Free cutting 110 26 90-220 Copper alloys Brass 90 27 90-220 Electrolitic copper 100 28 90-220 Non-metallic Duroplastics fiber plastics 29 Hard rubber 30 Fe based Annealed 200 31 30-60 Cured 280 32 20-50 High Lemp. alloys Ni or Co based Annealed 250 33 20-50 S Cured 350 34 20-50 Cast 320 35 20-50 Titanium Ti alloys Rm 400 36 20-50 Alpha+beta alloys cured Rm 1050 37 20-50 Hardened steel Hardened 55HRC 38 20-50 H Hardened 60HRC 39 20-50 Chilled cast iron Cast 400 40 Cast iron nodular Hardened 55HRC 41 Steel Stainless steel Cast iron Nonferrous High temp. alloys Hardened steel